A summary of some pertinent previous research by
other authors is presented separately from the actual
laboratory report. The report presents the results of air
and corrosion fatigue tests which are. interpreted in terms
of time to failure, crack growth history, and fracture
mechanics techniques. In addition, the results of cathodic
protection of corrosion fatigue tests are interpreted in
terms of simple-design criteria, as well as relative to
Critical Corrosion Rate Theory. One of the more significant
results presented is the greater longevity of corrosion
fatigue, as compared to air fatigue, notched specimens
stressed within 10-15 KSI above the air endurance limit.
Also, the potential required to cathodically protect such
notched specimens is shown to be 50 mV lower than for
comparable smooth specimens. Both phenomena are attributed
in part to the lowering of crack pH to acidic levels in
notched specimens.
other authors is presented separately from the actual
laboratory report. The report presents the results of air
and corrosion fatigue tests which are. interpreted in terms
of time to failure, crack growth history, and fracture
mechanics techniques. In addition, the results of cathodic
protection of corrosion fatigue tests are interpreted in
terms of simple-design criteria, as well as relative to
Critical Corrosion Rate Theory. One of the more significant
results presented is the greater longevity of corrosion
fatigue, as compared to air fatigue, notched specimens
stressed within 10-15 KSI above the air endurance limit.
Also, the potential required to cathodically protect such
notched specimens is shown to be 50 mV lower than for
comparable smooth specimens. Both phenomena are attributed
in part to the lowering of crack pH to acidic levels in
notched specimens.
Language
Type
Form
Extent
163 p.
Subject (Topical)
Identifier
13768
Additional Information
College of Engineering and Computer Science
Thesis (M.S.E.)--Florida Atlantic University, 1976.
FAU Electronic Theses and Dissertations Collection
Date Backup
1976
Date Text
1976
Date Issued (EDTF)
1976
Extension
FAU
FAU
admin_unit="FAU01", ingest_id="ing1508", creator="staff:fcllz", creation_date="2007-07-19 01:35:44", modified_by="staff:fcllz", modification_date="2011-01-06 13:09:02"
IID
FADT13768
Issuance
monographic
Organizations
Attributed name: Florida Atlantic University
Person Preferred Name
FLUET, JOSEPH E., JR.
Graduate College
Physical Description
163 p.
application/pdf
Title Plain
CORROSION FATIGUE OF NOTCHED 1018 STEEL IN SEA WATER
Use and Reproduction
Copyright © is held by the author, with permission granted to Florida Atlantic University to digitize, archive and distribute this item for non-profit research and educational purposes. Any reuse of this item in excess of fair use or other copyright exemptions requires permission of the copyright holder.
http://rightsstatements.org/vocab/InC/1.0/
Origin Information
1976
monographic
Boca Raton, Fla.
Florida Atlantic University
Physical Location
Florida Atlantic University Libraries
Place
Boca Raton, Fla.
Sub Location
Digital Library
Title
CORROSION FATIGUE OF NOTCHED 1018 STEEL IN SEA WATER
Other Title Info
CORROSION FATIGUE OF NOTCHED 1018 STEEL IN SEA WATER