Evaluation of carbon fiber/polyetheretherketone composites exposed to marine microbial communities in laboratory media and natural seawater

This research proposed to characterize any microbial induced degradation of carbon fiber/polyetheretherketone (PEEK) composites from acid-producing bacteria (APB) and sulfate-reducing bacteria (SRB). Electrochemical impedance spectroscopy (EIS) was used to provide a measure of degradation of the composite system as a function of exposure time. In addition, mechanical testing and microscopic evaluation of the specimens were utilized to determine if changes in the EIS spectra as a function of exposure time correlated to changes in the mechanical properties. Results from most EIS scans were consistent with a well-consolidated and undamaged composite system. Changes in the EIS response of specimens exposed to the SRB environment were not matched by a reduction in the flexural strength. Mechanical testing also indicated no reduction in the flexural strength in any of the other exposure environments. Environmental scanning electron microscopy (ESEM)/energy dispersive x-ray spectroscopy (EDS) were inconclusive, though changes in the EDS spectra were seen. No definitive degradation was seen to occur in this composite system.