Deterioration

This study investigates corrosion initiation and propagation in instrumented specimens obtained from segments of dry-cast reinforced concrete pipes. Potential, LPR and EIS measurements were carried out. During the propagation stage in different exposures, reinforcement eventually reached negative potentials values, which suggest mass transfer limitations. So far these specimens show no visual signs of corrosion such as cracks or corrosion products with one exception; where corrosion products have reached the surface. Moreover, the apparent corrosion rate values obtained suggest high corrosion rate. No crack appearance so far, could be explained by the high porosity of the specimens; the corrosion products are filling these pores. It is speculated that although, there might be mass transfer limitations present, the current demanded by the anode is being balanced by a larger cathode area due to macrocell effects, since the high moisture conditions likely reduced the concrete resistivity and increased the throwing power.

An experimental investigation was undertaken to determine the effects of marine environmental exposure on the mechanical properties of vinylester resins (VE510A and VE8084) and carbon fiber/VE510A vinylester composites. The effect of carbon fiber sizing on the composite strengths was also examined. Neat resins were exposed to marine environments until moisture content reached a point of saturation after which they were tested in tension, compression and shear. Compared to the baseline dry specimens, specimens subjected to moisture showed overall increased ductility and a reduction in strength. Dry and moisture saturated composite specimens were tested in tension and compression in different orientations. Longitudinal specimens were tested in in-plane shear and interlaminar shear. Composites with F-sized carbon fibers displayed overall higher strength than those with G-sized fibers at both dry and moisture saturated conditions. An analysis of moisture absorption of the composites was performed which vii shows that the moisture up-take is dominated by the fiber/matrix region which absorbs up to 90% of the moisture. The composites experienced reduced strength after moisture absorption. The results revealed that the fiber sizing has stronger effect on the fiber/matrix interface dominated strengths than moisture up-take.

Durability of the composite materials in marine environments has been investigated experimentally and with analytical and numerical methods. The main focus of this study is on the integrity of the fiber/matrix interface under seawater exposure. A single-fiber compression test specimen called the Outwater-Murphy (OM) test has been analyzed using mechanics of materials principles and linear elastic fracture mechanics. Sizing of the OM specimen was conducted so that debonding of the fiber from the interface should be achieved prior to yielding of the matrix and global instability failure. Stress analysis of the OM specimen has been conducted from theory of elasticity and finite element analysis. A superelement technique was developed for detailed analysis of the stress state at the fiber/matrix interface. The interface stress state at the debond site in the OM specimen, i.e. at the hole edge, was identified as biaxial tension at the fiber/matrix interface. Characterization of cure and post-cure of 8084 and 510A vinlyester resins has been performed using cure shrinkage tests based on dynamic mechanical analysis and coated beam experiments. In addition, moisture absorption, swelling and the influence of moisture on the mechanical properties of the resins were determined. Testing of OM specimens consisting of a single carbon or glass fiber embedded in vinylester resin at dry conditions and after seawater exposure revealed that the debond toughness was substantially reduced after exposure of the OM specimen to seawater. C(F) did not debond. Macroscopic carbon/vinylester woven composites where the fibers were sized with F sizing were tested in shear at dry conditions and after four weeks of seawater exposure. The shear strength was very little affected after the short immersion time.