Mechanical properties

In recent years, high strength concrete (HSC) is becoming an attractive alternative to traditional normal strength concrete (NSC), and is used in a wide range of applications. With the increased use of HSC, concern has developed regarding the behavior of such concrete in fire. Until now, the fire performance of HSC is not fully understood and more research is needed. Full-scale fire testing is time consuming and expensive, and the real fire scenario is different from the standard fire. Performance-based assessment methods, including numerical analysis and simplified method, are being accepted in an increasing number of countries. In this dissertation, the fire testing results both of HSC and NSC are presented, performance-based numerical models are developed to study the fire performance of reinforced concrete (RC) members, and simplified calculation methods are proposed to estimate the load capacity of fire-damaged RC columns/beams. A detailed and comprehensive literature review is presented that provides background information on the high temperature behavior of concrete materials and RC members, as well as information on fire performance assessment procedures and objectives. The fire testing results of seven batches of HSC and NSC are presented and discussed. The test results indicated that the post-fire re-curing results in substantial strength and durability recovery, and its extent depends upon the types of concrete, temperature level, and re-curing age. The fire tests also showed that violent explosive reduced the risk of HSC explosive spalling. The surface crack widths were also reduced during the re-curing process, and in most cases, they were found within the maximum limits specified by the American Concrete Institute (ACI) building code.

In this investigation, polymer precursor of syntactic foam has been reinforced with SiC nanoparticles to enhance mechanical and fracture properties. Derakane 8084 vinyl ester resin was first dispersed with 1.0 wt% of SiC particles using a sonic cavitation technique. In the next step, 30.0 wt% of microspheres (3M hollow glass borosilicate, S-series) were mechanically mixed with the nanophased vinyl ester resin, and cast into rectangular molds. A small amount of styrene was used as dilutant to facilitate mixing of microspheres. The size of microspheres and SiC nanoparticles were 20-30 um and 30-50 nm, respectively. Tension, compression, and flexure tests were conducted following ASTM standards and a consistent improvement in strength and modulus within 20-35% range was observed. Fracture toughness parameters such as KIC and GIC were also determined using ASTM E-399. An improvement of about 11-15% was observed. Samples were also subjected to various environmental conditions and degradation in material properties is reported.

This study is to compare the performance of recycled aggregate concrete and the impact of up to 50% cement replacement with fly ash on durability. Water content, sieve analysis, standard and modified compaction tests were performed to assess the physical properties of the recycled aggregate concrete. Accelerated aging tests were performed to predict the long term durability of the recycled aggregate concrete. Following Arrhenius modeling and TTS and SIM accelerated aging protocols, a time versus stiffness master curve was created. This allowed the prediction of equivalent age using experimental data and theoretical analysis. To account for environmental exposure, the specimens underwent 24 and 48 hours of wet-dry cycling and subjected. Overall there was an increase in stiffness and strength from the specimens containing fly ash. All tests performed predicted equivalent age beyond the testing period of 144 hrs. and up to 7 years. Specimens containing fly maintained a constant and higher density to environmental exposure.

Enhancement of mechanical, thermal and hygrothermal properties of carbon fiber/vinyl ester (CFVE) composites through nanoparticle reinforcement has been investigated. CFVE composites are becoming more and more attractive for marine applications due to two reasons : high specific strength and modulus of carbon fiber and low vulnerability of vinyl ester resin to sea water. However, the problem with this composite system is that the fiber matrix (F/M) interface is inherently weak. This leads to poor mechanical properties and fast ingress of water at the interface further deteriorating the properties. This investigation attempts to address these deficiencies by inclusion of nanoparticles in CFVE composites. Three routes of nanoparticle reinforcement have been considered : nanoparticle coating of the carbon fiber, dispersion of nanoparticles in the vinyl ester matrix, and nanoparticle modification of both the fiber and the matrix. Flexural, short beam shear and tensile testing was conducted after exposure to dry and wet environments. Differential scanning calorimetry and dynamic mechanical analysis were conducted as well. Mechanical and thermal tests show that single inclusion of nanoparticles on the fiber or in the matrix increases carbon/vinyl ester composite properties by 11-35%. However, when both fiber and matrix were modified with nanoparticles, there was a loss of properties.

An experimental investigation was undertaken to determine the effects of marine environmental exposure on the mechanical properties of vinylester resins (VE510A and VE8084) and carbon fiber/VE510A vinylester composites. The effect of carbon fiber sizing on the composite strengths was also examined. Neat resins were exposed to marine environments until moisture content reached a point of saturation after which they were tested in tension, compression and shear. Compared to the baseline dry specimens, specimens subjected to moisture showed overall increased ductility and a reduction in strength. Dry and moisture saturated composite specimens were tested in tension and compression in different orientations. Longitudinal specimens were tested in in-plane shear and interlaminar shear. Composites with F-sized carbon fibers displayed overall higher strength than those with G-sized fibers at both dry and moisture saturated conditions. An analysis of moisture absorption of the composites was performed which vii shows that the moisture up-take is dominated by the fiber/matrix region which absorbs up to 90% of the moisture. The composites experienced reduced strength after moisture absorption. The results revealed that the fiber sizing has stronger effect on the fiber/matrix interface dominated strengths than moisture up-take.

Degradation of the Carbon Fiber/Vinylester (CF/VE) polymer matrix composites due to different electrochemical interactions when exposed to seawater or at high temperature had been experimentally investigated. Water uptake behavior of composite specimen was examined based on weight gain measurement. Three point bending test was performed to quantify the mechanical degradation of composite immersed in seawater with different environmental and electrochemical interactions. Finally, Electrochemical Impedance Spectroscopy (EIS) was used to better understanding of the degradation process in CF/VE composite produced by interactions between electrochemical and different environmental conditions. A detailed equivalent circuit analysis by using EIS spectra is also presented in an attempt to elucidate the degradation phenomenon in composites.

Durability of the composite materials in marine environments has been investigated experimentally and with analytical and numerical methods. The main focus of this study is on the integrity of the fiber/matrix interface under seawater exposure. A single-fiber compression test specimen called the Outwater-Murphy (OM) test has been analyzed using mechanics of materials principles and linear elastic fracture mechanics. Sizing of the OM specimen was conducted so that debonding of the fiber from the interface should be achieved prior to yielding of the matrix and global instability failure. Stress analysis of the OM specimen has been conducted from theory of elasticity and finite element analysis. A superelement technique was developed for detailed analysis of the stress state at the fiber/matrix interface. The interface stress state at the debond site in the OM specimen, i.e. at the hole edge, was identified as biaxial tension at the fiber/matrix interface. Characterization of cure and post-cure of 8084 and 510A vinlyester resins has been performed using cure shrinkage tests based on dynamic mechanical analysis and coated beam experiments. In addition, moisture absorption, swelling and the influence of moisture on the mechanical properties of the resins were determined. Testing of OM specimens consisting of a single carbon or glass fiber embedded in vinylester resin at dry conditions and after seawater exposure revealed that the debond toughness was substantially reduced after exposure of the OM specimen to seawater. C(F) did not debond. Macroscopic carbon/vinylester woven composites where the fibers were sized with F sizing were tested in shear at dry conditions and after four weeks of seawater exposure. The shear strength was very little affected after the short immersion time.

In this research, the degradation of carbon fiber/vinylester composites in marine environments was experimentally investigated. Additionally, two types of carbon fiber surface treatments, namely Polyhedral Oligomeric Silsesquioxane (POSS) and the industrial surface treatment F0E, were evaluated to determine their effectiveness in creating a fiber/matrix (F/M) interface for use in the marine environment. Electrochemical Impedance Spectroscopy (EIS) was explored as a new application of an existing technique for use in measuring the amount of water at the F/M interface in carbon fiber/vinylester composites. EIS spectra were used to determine equivalent electric circuit models that allow for the prediction of water at the interface. The location of water within the composite was determined through Positron Annihilation Lifetime Spectroscopy (PALS). Interlaminar shear strength and transverse tensile tests were carried out for dry conditions and after hygrothermal exposure of the composites to study the influence of the integrity of the F/M interface on the macroscopic response of the composite.